Description:
PB681/59 is a grade produced under high pressure in a tubular reactor. This resin is used for laminating films mainly on paper substrate. It is also used in the extrusion coating process. Films obtained with this product show excellent optical properties and high draw down ability.
Additive:
-Antiblock Medium
-Slip High
Applications:
Lamination film; general purpose.
材料物性
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.922 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 38 | µm | |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂 | 30.0 | MPa | ASTM D882 |
| TD : 断裂 | 20.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂 | 340 | % | ASTM D882 |
| TD : 断裂 | 1100 | % | ASTM D882 |
| 落锤冲击 | 60 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 - TD | 100 | g | ASTM D1922 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (60°) | 112 | ASTM D2457 | |
| 雾度 | 5.0 | % | ASTM D1003 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒1区温度 | 110 | °C | |
| 口模温度 | 150 | °C |
| 挤压说明 |
|---|
| Blown FilmScrew L/D relation: 16 to 30:1Compression rate: 3 to 4:1Screen package(Mesh): 40/60/40Extruder: 140°CBlow up ratio: 2 to 3:1Frostline height: at most equivalent to the bubble diameter |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE SGM9450F | HDPE | Braskem | 高分子量,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA,中等宽分子量分布 |
| Braskem PE SHC7260 | HDPE | Braskem | 低翘曲性,刚性，高,可更新资源,食品接触的合规性,无 BPA,硬度高 |
| Braskem PE SGM7746C | HDPE | Braskem | 高 ESCR（抗应力开裂）,高分子量,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA |
| Braskem PE SHA7260 | HDPE | Braskem | 低翘曲性,刚性，高,可更新资源,可加工性，良好,良好的流动性,食品接触的合规性,无 BPA,硬度高,窄分子量分布 |
| Braskem PE SGF4960 | HDPE | Braskem | 刚性，高,高密度,均聚物,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA |