HDPE Braskem PE SGM7746C 高 ESCR（抗应力开裂）,高分子量,抗撞击性，
材料简述：
SGM7746C is a High Density Polyethylene specially developed for the manufacturing of blow molding fuel tanks. It has high molar mass and excellent mechanical properties. Besides, it shows excellent tenacity, high resistance to stress cracking, and outstanding impact resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866.
材料物性
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.944 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/21.6 kg) | 4.5 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 1(50°C, 2.00 mm, 100% Igepal, 模压成型, F50) | > 1000 | hr | ASTM D1693 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 模压成型) | 62 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服, 模压成型 | 23.0 | MPa | ASTM D638 |
| 断裂, 模压成型 | 42.0 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服, 模压成型 | 13 | % | ASTM D638 |
| 断裂, 模压成型 | 880 | % | ASTM D638 |
| 弯曲模量 - 1% 正割 (模压成型) | 890 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 (模压成型) | 760 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 (0.45 MPa, 未退火, 模压成型) | 70.0 | °C | ASTM D648 |
| 维卡软化温度 | 126 | °C | ASTM D1525 2 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 生物质含量 | > 96 | % | ASTM D6866 |
| 备注 | |
|---|---|
| 1 . | 0.3 mm notched-plaques |
| 2 . | 压 力1 (10N) |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE SHA7260 | HDPE | Braskem | 低翘曲性,刚性，高,可更新资源,可加工性，良好,良好的流动性,食品接触的合规性,无 BPA,硬度高,窄分子量分布 |
| Braskem PE SGF4960 | HDPE | Braskem | 刚性，高,高密度,均聚物,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA |
| Braskem PE SGF4950 | HDPE | Braskem | 刚性，良好,高 ESCR（抗应力开裂）,共聚物,抗撞击性，良好,可更新资源,可加工性，良好,食品接触的合规性,无 BPA |
| Braskem PE PB-608 | LDPE | Braskem | 低密度,良好的流动性,良好的柔韧性,耐高压加热性 |
| Braskem PE MR-435UV | LLDPE | Braskem | 低密度,丁烯共聚单体,刚性，良好,高 ESCR（抗应力开裂）,可加工性，良好 |