材料简述：

---

SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process.
The minimum biobased content of this grade is 96%, determined according to ASTM D6866.

Application:
Bags in general (like T-shirt bags, Handle Bags, Star Bags, others); Geomembranes.

材料物性

基本信息
特性	高分子量 抗撞击性，高 可更新资源 食品接触的合规性 无 BPA 中等宽分子量分布
用途	Geo Membranes 包装 薄膜 袋子
机构评级	ASTM D 6866 FDA 21 CFR 177.1520
形式	粒子
加工方法	薄膜挤出 吹塑薄膜

物理性能	额定值	单位制	测试方法
比重	0.952	g/cm³	ASTM D792
熔流率（熔体流动速率）			ASTM D1238
190°C/21.6 kg	9.3	g/10 min	ASTM D1238
190°C/5.0 kg	0.33	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	13	µm
抗张强度			ASTM D882
MD : 屈服, 13 µm, 吹塑薄膜	40.0	MPa	ASTM D882
TD : 屈服, 13 µm, 吹塑薄膜	30.0	MPa	ASTM D882
MD : 断裂, 13 µm, 吹塑薄膜	85.0	MPa	ASTM D882
TD : 断裂, 13 µm, 吹塑薄膜	45.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 13 µm, 吹塑薄膜	590	%	ASTM D882
TD : 断裂, 13 µm, 吹塑薄膜	740	%	ASTM D882
落锤冲击 1(13 µm, 吹塑薄膜)	250	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 13 µm, 吹塑薄膜	58	g	ASTM D1922
TD : 13 µm, 吹塑薄膜	51	g	ASTM D1922
始封温度 (13 µm, 吹塑薄膜)	125	°C	内部方法

补充信息	额定值	单位制	测试方法
Puncture Resistance - Blown Film (12.5 µm)	80.0	J/m	内部方法
生物质含量	> 96	%	ASTM D6866

备注
1 .	F50

相关牌号	种类	厂家	特性
Braskem PE SHC7260	HDPE	Braskem	低翘曲性,刚性，高,可更新资源,食品接触的合规性,无 BPA,硬度高
Braskem PE SGM7746C	HDPE	Braskem	高 ESCR（抗应力开裂）,高分子量,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA
Braskem PE SHA7260	HDPE	Braskem	低翘曲性,刚性，高,可更新资源,可加工性，良好,良好的流动性,食品接触的合规性,无 BPA,硬度高,窄分子量分布
Braskem PE SGF4960	HDPE	Braskem	刚性，高,高密度,均聚物,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA
Braskem PE SGF4950	HDPE	Braskem	刚性，良好,高 ESCR（抗应力开裂）,共聚物,抗撞击性，良好,可更新资源,可加工性，良好,食品接触的合规性,无 BPA