材料简述：

---

Pluris4303 is a Braskem Quaterpolymer produced with Spherilene technology. This grade show unique properties, such as high stiffness associated with toughness. In addition to good processability, also shows a very good bubble stability and very low gel content.

Applications:
Thin films and automatic packaging which require higher stiffness: textile products, toilet paper and others.

Additive:
Antiblocking medium
Slip medium

Process:
Blown Film Extrusion

材料物性

基本信息
添加剂	中等抗结块性 中度光滑性
特性	低速凝固晶点 刚性，高 可加工性，良好 韧性良好 中等抗结块性 中度光滑性
用途	Blown Film 包装 薄膜
机构评级	FDA 21 CFR 177.1520
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
比重	0.922	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	1.8	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 断裂, 40 µm, 吹塑薄膜	30.0	MPa	ASTM D882
TD : 断裂, 40 µm, 吹塑薄膜	20.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 40 µm, 吹塑薄膜	700	%	ASTM D882
TD : 断裂, 40 µm, 吹塑薄膜	1300	%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD : 40 µm, Blown Film	240	MPa	ASTM D790
1% Secant, TD : 40 µm, Blown Film	300	MPa	ASTM D790
埃尔曼多夫抗撕强度			ASTM D1922
MD : 40 µm, 吹塑薄膜	30	g	ASTM D1922
TD : 40 µm, 吹塑薄膜	1100	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (60°, 40.0 µm, 吹塑薄膜)	57		ASTM D2457
雾度 (40.0 µm, 吹塑薄膜)	15	%	ASTM D1003

相关牌号	种类	厂家	特性
Braskem PE LL4405S	LLDPE	Braskem	低速凝固晶点,高光滑性,高抗结块性,可加工性，良好
Braskem PE LL4801N	LLDPE	Braskem	光学性能,抗氧化性,可加工性，良好
Braskem PE LL5400S	LLDPE	Braskem	低速凝固晶点,光学性能,抗氧化性,可加工性，良好
Braskem PE LL5405S	LLDPE	Braskem	低速凝固晶点,高光滑性,高抗结块性,可加工性，良好
Braskem PE PROXESS 2606	LLDPE	Braskem	高强度,抗氧化性,清晰度，高