材料简述：

---

LL5405S is a Linear Low Density Polyethylene (LLDPE) developed for blown film extrusion. Films obtained with this product show a good processing performance balanced with good mechanical properties as well as processability. Very low gel amount.

Additive:
Antiblocking ­ High
Slip - High

Applications:
LLDPE and HDPE blends, films with low thickness for general use, bags for waste, special bags for water and protection of clothes.

Process:
Blown film extrusion.

材料物性

基本信息
添加剂	高光滑性 高抗结块性
特性	低速凝固晶点 高光滑性 高抗结块性 可加工性，良好
用途	Blown Film 薄膜 袋子 混合
机构评级	FDA 21 CFR 177.1520
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
比重	0.919	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

机械性能	额定值	单位制	测试方法
摩擦系数 (吹塑薄膜)	0.10		ASTM D1894

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 断裂, 40 µm, 吹塑薄膜	35.0	MPa	ASTM D882
TD : 断裂, 40 µm, 吹塑薄膜	25.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 40 µm, 吹塑薄膜	1000	%	ASTM D882
TD : 断裂, 40 µm, 吹塑薄膜	1200	%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD : 40 µm, Blown Film	160	MPa	ASTM D790
1% Secant, TD : 40 µm, Blown Film	180	MPa	ASTM D790
落锤冲击 (40 µm, 吹塑薄膜)	120	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 40 µm, 吹塑薄膜	90	g	ASTM D1922
TD : 40 µm, 吹塑薄膜	900	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度			ASTM D2457
45°, 40.0 µm, 吹塑薄膜	55		ASTM D2457
60°, 40.0 µm, 吹塑薄膜	80		ASTM D2457
雾度 (40.0 µm, 吹塑薄膜)	18	%	ASTM D1003

补充信息	额定值	单位制	测试方法
Blocking 1(40.0 µm)	8.00	g/100 cm²	ASTM D3354

备注
1 .	Blown Film

相关牌号	种类	厂家	特性
Braskem PE PROXESS 2606	LLDPE	Braskem	高强度,抗氧化性,清晰度，高
Braskem PE FLEXUS7200XP	LLDPE	Braskem	光学性能,抗氧化性,可加工性，良好
Braskem PE ML3602U	LLDPE	Braskem	UV Stabilized,刚性，良好,抗氧化性,抗撞击性，良好,可加工性，良好,热稳定性,优良外观
Braskem PE HF2208S3	LLDPE	Braskem	光滑性,抗结块性,抗氧化性
Braskem PE LF1020/21AF	LLDPE	Braskem	可加工性，良好,中等抗结块性,中度光滑性