材料简述：

---

LL5400S is a Linear Low Density Polyethylene developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives.

Applications:
Liners; LDPE and HDPE blends and packages for general use.
Others applications: blends for irrigation pipes.

Process:
Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.

材料物性

基本信息
添加剂	抗氧化性
特性	低速凝固晶点 光学性能 抗氧化性 可加工性，良好
用途	Blown Film 包装 薄膜 衬里 管道系统 混合
机构评级	FDA 21 CFR 177.1520
加工方法	薄膜挤出 吹塑薄膜

物理性能	额定值	单位制	测试方法
密度	0.918	g/cm³	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 断裂, 38 µm, 吹塑薄膜	40.0	MPa	ASTM D882
TD : 断裂, 38 µm, 吹塑薄膜	30.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 38 µm, 吹塑薄膜	1100	%	ASTM D882
TD : 断裂, 38 µm, 吹塑薄膜	1400	%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD : 38 µm, Blown Film	170	MPa	ASTM D790
1% Secant, TD : 38 µm, Blown Film	200	MPa	ASTM D790
落锤冲击 (38 µm, 吹塑薄膜)	120	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 38 µm, 吹塑薄膜	100	g	ASTM D1922
TD : 38 µm, 吹塑薄膜	400	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (60°, 38.0 µm, 吹塑薄膜)	110		ASTM D2457
雾度 (38.0 µm, 吹塑薄膜)	10	%	ASTM D1003

相关牌号	种类	厂家	特性
Braskem PE LL5405S	LLDPE	Braskem	低速凝固晶点,高光滑性,高抗结块性,可加工性，良好
Braskem PE PROXESS 2606	LLDPE	Braskem	高强度,抗氧化性,清晰度，高
Braskem PE FLEXUS7200XP	LLDPE	Braskem	光学性能,抗氧化性,可加工性，良好
Braskem PE ML3602U	LLDPE	Braskem	UV Stabilized,刚性，良好,抗氧化性,抗撞击性，良好,可加工性，良好,热稳定性,优良外观
Braskem PE HF2208S3	LLDPE	Braskem	光滑性,抗结块性,抗氧化性