材料简述：

---

Braskem PROXESS2606 is a linear low density polyethylene (LLDPE) produced through metallocene catalyst and recommended to blown film extrusion. Films obtained with this grade exhibits high mechanical strength, better sealing, high transparency and comparable contraction levels. These properties make this product a versatile option for both monolayer and multilayer films.

Applications:
Shrink films, industrial sacks, ice, sand and mortar packing.

Additives:
Antioxidants
Processing Aid

Process:
Blown Films Extrusion

材料物性

基本信息
添加剂	加工助剂 抗氧化性
特性	高强度 抗氧化性 清晰度，高
用途	Blown Film 包装 薄膜 多层薄膜 工业应用 收缩性薄膜 重包装袋
机构评级	FDA 21 CFR 177.1520
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
比重	0.926	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	0.60	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 断裂, 100 µm, 吹塑薄膜	40.0	MPa	ASTM D882
TD : 断裂, 100 µm, 吹塑薄膜	30.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 100 µm, 吹塑薄膜	1000	%	ASTM D882
TD : 断裂, 100 µm, 吹塑薄膜	1100	%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD : 100 µm, Blown Film	240	MPa	ASTM D790
1% Secant, TD : 100 µm, Blown Film	250	MPa	ASTM D790
落锤冲击 (100 µm, 吹塑薄膜)	560	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 100 µm, 吹塑薄膜	480	g	ASTM D1922
TD : 100 µm, 吹塑薄膜	1900	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (45°, 100 µm, 吹塑薄膜)	66		ASTM D2457
雾度 (100 µm, 吹塑薄膜)	12	%	ASTM D1003

相关牌号	种类	厂家	特性
Braskem PE FLEXUS7200XP	LLDPE	Braskem	光学性能,抗氧化性,可加工性，良好
Braskem PE ML3602U	LLDPE	Braskem	UV Stabilized,刚性，良好,抗氧化性,抗撞击性，良好,可加工性，良好,热稳定性,优良外观
Braskem PE HF2208S3	LLDPE	Braskem	光滑性,抗结块性,抗氧化性
Braskem PE LF1020/21AF	LLDPE	Braskem	可加工性，良好,中等抗结块性,中度光滑性
Braskem PE LF321FC	LLDPE	Braskem	低速凝固晶点,可交联