LLDPE Braskem PE HF2208S3 光滑性,抗结块性,抗氧化性
材料简述：
The HF2208S3 resin is a linear low density polyethylene, developed for blown film extrusion with good mechanical properties.
Applications:
High-performance technical films for automatic packaging of liquids and solids, co-extrusion and general uses
Additive:
Antioxidant
Slip
Anti-blocking
Processing Aid
Process:
The HF2208S3 needs to be processed in blown film extruder. The optimum processing conditions are obtained with extrusion temperature between 200 to 220°C blended with 30% of low density polyethylene.
材料物性
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.922 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD | 210 | MPa | ASTM D882 |
| 1% 正割, TD | 240 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂 | 45.0 | MPa | ASTM D882 |
| TD : 断裂 | 30.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂 | 950 | % | ASTM D882 |
| TD : 断裂 | 1200 | % | ASTM D882 |
| 落锤冲击 | 200 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD | 150 | g | ASTM D1922 |
| TD | 840 | g | ASTM D1922 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (45°) | 70 | ASTM D2457 | |
| 雾度 | 11 | % | ASTM D1003 |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE LF1020/21AF | LLDPE | Braskem | 可加工性，良好,中等抗结块性,中度光滑性 |
| Braskem PE LF321FC | LLDPE | Braskem | 低速凝固晶点,可交联 |
| Braskem PE SGF4950 | HDPE | Braskem | 刚性，良好,高 ESCR（抗应力开裂）,高密度,共聚物,抗撞击性，良好,可更新资源,可加工性，良好,食品接触的合规性 |
| Braskem PE SGF4960 | HDPE | Braskem | 刚性，高,高密度,均聚物,抗撞击性，高,可更新资源,食品接触的合规性 |
| Braskem PE SHA7260 | HDPE | Braskem | 低翘曲性,刚性，高,可更新资源,可加工性，良好,良好的流动性,食品接触的合规性,硬度高,窄分子量分布 |