材料简述：

---

Pluris4301 is a Braskem Quaterpolymer produced with Spherilene technology. This grade show unique properties, such as high stiffness associated with toughness. In addition to good processability, also shows a very good bubble stability and very low gel content.

Applications:
Thin films and automatic packaging which require higher stiffness: textile products, toilet paper and others.

Additive:

• Antiblocking medium

• Slip medium

Process:
Blown Film Extrusion

材料物性

基本信息
添加剂	中等抗结块性 中度光滑性
特性	低密度 低速凝固晶点 刚性，高 可加工性，良好 中等抗结块性 中度光滑性
用途	包装 薄膜
机构评级	FDA 21 CFR 177.1520
形式	粒子
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
比重	0.922	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	1.8	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 断裂, 38 µm	32.0	MPa	ASTM D882
TD : 断裂, 38 µm	33.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 38 µm	920	%	ASTM D882
TD : 断裂, 38 µm	1500	%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD : 38 µm	310	MPa	ASTM D790
1% Secant, TD : 38 µm	400	MPa	ASTM D790
埃尔曼多夫抗撕强度			ASTM D1922
MD : 38 µm	50	g	ASTM D1922
TD : 38 µm	300	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (60°, 38.0 µm)	45		ASTM D2457
雾度	43	%	ASTM D1003

挤压说明
Recommended Blown Film Extrusion Conditions: Temperature Profile: 150°C to 170°C Blow Up Ratio: 2 to 3:1 Die Gap: 1.8 to 2.5 mm Mass Temperature: 160° to 200°C It's Recommended to add 20 to 30% LDPE to be obtained excellent optical propert

相关牌号	种类	厂家	特性
Braskem PE PLURIS 9300	LLDPE	Braskem	低速凝固晶点,刚性，高,抗结块性,抗氧化性,可加工性，良好,韧性良好
Braskem PE PB-681/59	LDPE	Braskem	低密度,高光滑性,光学性能,良好的剥离性,中等抗结块性
Braskem PE SGM9450F	HDPE	Braskem	高分子量,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA,中等宽分子量分布
Braskem PE SHC7260	HDPE	Braskem	低翘曲性,刚性，高,可更新资源,食品接触的合规性,无 BPA,硬度高
Braskem PE SGM7746C	HDPE	Braskem	高 ESCR（抗应力开裂）,高分子量,抗撞击性，高,可更新资源,食品接触的合规性,无 BPA