HDPE Braskem PE HS5502 超强刚性,高密度,共聚物,可加工性，良好
材料简述：
HS5502 is a high density polyethylene, copolymer. Offers good processability and bottles produced have excellent stiffness.
Application:
Blow Molded Small Volume: Food, lubricant oils and pharmaceutical packing; Toys; Braskem does not recommend the use of HS5502 for the production of films.
Process:
Blow Molding;
Injection Blow Molding.
材料物性
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.955 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 190°C/2.16 kg | 0.35 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 32 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 1 | ASTM D1693 | ||
| 2.00 mm, 10% Igepal, 模压成型, F50 | 10.0 | hr | ASTM D1693 |
| 2.00 mm, 100% Igepal, 模压成型, F50 | 20.0 | hr | ASTM D1693 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (断裂, 模压成型) | 30.0 | MPa | ASTM D638 |
| 弯曲模量 - 1% 正割 (模压成型) | 1350 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 无缺口悬臂梁冲击 (模压成型) | 150 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 (0.45 MPa, 未退火, 模压成型) | 69.0 | °C | ASTM D648 |
| 注射说明 |
|---|
| Recommended Blow Molding Conditions: Feeding Zone: 185°C Barrel: 190°C Die: 195°C Mold Temperature: 5°C to 25°C Parison: 200°C |
| 备注 | |
|---|---|
| 1 . | 0.3mm notched-plaques |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE HS5608 | HDPE | Braskem | 超强刚性,高 ESCR（抗应力开裂）,高分子量,高密度,共聚物,抗撞击性，良好,食品接触的合规性 |
| Braskem PE GP 100OR | HDPE | Braskem | 高 ESCR（抗应力开裂）,高分子量,抗紫外线性能良好 |
| Braskem PE IN-34 | LLDPE | Braskem | 低翘曲性,丁烯共聚单体,共聚物,良好的柔韧性,流动性高,食品接触的合规性,窄分子量分布 |
| Braskem PE GM9450F | HDPE | Braskem | 高分子量,高密度,抗撞击性，高,可加工性，良好,宽分子量分布,食品接触的合规性 |
| Braskem PE IA 58 | HDPE | Braskem | 丁烯共聚单体,刚性，良好,高密度,共聚物,抗氧化性,抗撞击性，良好,可加工性，良好,食品接触的合规性,窄分子量分布 |