材料简述：

---

The GP 100 OR is a High Density Polyethylene compounding with high molar mass, specially developed for the manufacturing of extruded pipes for gas pressurized line. This resin is produced with bimodal technology, it has excellent mechanical properties and very high resistance to internal pressure. This resin has MRS (Minimum Required Strength) of 10 MPa according to ISO 9080, and is classified as PE 100 according to ISO 12162. GP 100 OR is manufactured in orange color and it contains additives that protect it against the action of ultraviolet radiation.

Meets the requirements of NBR 14462:00.

Application:
Orange PE 100 pressure pipes for gas distribution; jacketing of underwater cables

材料物性

基本信息
添加剂	紫外线稳定剂
特性	高 ESCR（抗应力开裂） 高分子量 抗紫外线性能良好
用途	管道系统 天然气输配
机构评级	ISO 12162 PE 100 ISO 9080 PE 100
外观	橙色
形式	粒子
加工方法	管路挤出成型 挤出

物理性能	额定值	单位制	测试方法
比重	0.950	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/5.0 kg)	0.22	g/10 min	ASTM D1238
抗环境应力开裂 (50°C, 2.00 mm, 100% Igepal, 模压成型, F50)	> 1000	hr	ASTM D1693

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 模压成型)	64		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 模压成型	24.0	MPa	ASTM D638
断裂, 模压成型	36.0	MPa	ASTM D638
伸长率			ASTM D638
屈服, 模压成型	8.1	%	ASTM D638
断裂, 模压成型	770	%	ASTM D638
弯曲模量 - 1% 正割 (模压成型)	1240	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (模压成型)	350	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度 (0.45 MPa, 未退火, 模压成型)	72.0	°C	ASTM D648
维卡软化温度	126	°C	ASTM D1525 1

备注
1 .	压 力1 (10N)

相关牌号	种类	厂家	特性
Braskem PE IN-34	LLDPE	Braskem	低翘曲性,丁烯共聚单体,共聚物,良好的柔韧性,流动性高,食品接触的合规性,窄分子量分布
Braskem PE GM9450F	HDPE	Braskem	高分子量,高密度,抗撞击性，高,可加工性，良好,宽分子量分布,食品接触的合规性
Braskem PE IA 58	HDPE	Braskem	丁烯共聚单体,刚性，良好,高密度,共聚物,抗氧化性,抗撞击性，良好,可加工性，良好,食品接触的合规性,窄分子量分布
Braskem PE F-2022/0	LDPE	Braskem	高 ESCR（抗应力开裂）,光学性能
Braskem PE F 7018	LDPE	Braskem	低温热封性,低粘度,可加工性，良好,通用