LDPE Braskem PE PB-681 低密度,光学性能,良好的剥离性
材料简述：
Description:
The PB681 is a resin produced under high pressure, in tubular reactor. This resin presents excellent 'draw down'(stability to form fine films). The films produced with this resin present excellent optical properties.
Applications:
LLDPE and HDPE blends.
Process:
Blown Film Extrusion
Cast Film Extrusion
Injection Moulding
材料物性
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.922 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 38 | µm | |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂 | 30.0 | MPa | ASTM D882 |
| TD : 断裂 | 20.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂 | 370 | % | ASTM D882 |
| TD : 断裂 | 1100 | % | ASTM D882 |
| 落锤冲击 | 60 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 - TD | 100 | g | ASTM D1922 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (60°) | 120 | ASTM D2457 | |
| 雾度 | 4.0 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 加工（熔体）温度 | 180 到 220 | °C | |
| 模具温度 | 5.00 到 25.0 | °C |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒1区温度 | 110 | °C | |
| 口模温度 | 150 | °C |
| 挤压说明 |
|---|
| Blown FilmScrew L/D relation: 16 to 30:1Compression rate: 3 to 4:1Screen package(Mesh): 40/60/40From the screw to the die: 140°CBlow up ratio: 2 to 3:1Frostline height: at most equivalent to the bubble diameterCast FilmScrew L/D relation: at least 20:1Screw: 180 to 250°CDie: 250 to 290°CChill roll: 40°C |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE PB-682 | LDPE | Braskem | 尺寸稳定性良好,低密度,良好的柔韧性 |
| Braskem PE S 1522 | LDPE | Braskem | 高 ESCR（抗应力开裂）,良好的热封性,通用 |
| Braskem PE PLURIS4301 | LLDPE | Braskem | 低密度,低速凝固晶点,刚性，高,可加工性，良好,中等抗结块性,中度光滑性 |
| Braskem PE PLURIS 9300 | LLDPE | Braskem | 低速凝固晶点,刚性，高,抗结块性,抗氧化性,可加工性，良好,韧性良好 |
| Braskem PE PB-681/59 | LDPE | Braskem | 低密度,高光滑性,光学性能,良好的剥离性,中等抗结块性 |