材料简述：

---

EF2002 is a low-density polyethylene (LDPE) with high molecular weight. Has excellent processability, proper of branched polyethylene produced by a high-pressure process. EF2002 resin presents an excellent performance in conventional LDPE extruders, granting low energy consumption during the whole process and allowing the production of packaging with a good dimensional uniformity and an excellent surface finishing.

Application:
High resistance films for industrial packaging, heavy duty bags and plastic canvas. Base resin for agriculture films with big dimensions.

Process:
Blown Film Extrusion

材料物性

基本信息
特性	尺寸稳定性良好 低密度 高分子量 可加工性，良好 优良外观
用途	包装 农业应用 重包装袋
机构评级	FDA 21 CFR 177.1520
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
比重	0.920	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	0.16	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
割线模量			ASTM D882
2% 正割, MD : 50 µm	150	MPa	ASTM D882
2% 正割, TD : 50 µm	170	MPa	ASTM D882
抗张强度			ASTM D882
MD : 断裂, 50 µm	30.0	MPa	ASTM D882
TD : 断裂, 50 µm	25.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 50 µm	360	%	ASTM D882
TD : 断裂, 50 µm	740	%	ASTM D882
落锤冲击 1(50 µm)	200	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 50 µm	180	g	ASTM D1922
TD : 50 µm	200	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (60°, 50.0 µm)	53		ASTM D2457
雾度	19	%	ASTM D1003

挤压说明
Recommended Blow Film Extrusion Conditions: Temperature Profile: 170°C to 225°C Mass Temperature: 190°C to 225°C Blow up Ratio: 2.0 to 3.0 : 1 Die Gap: 1.0 to 1.5 mm

备注
1 .	F50

相关牌号	种类	厂家	特性
Braskem PE ES6004	HDPE	Braskem	刚性，高,高密度,均聚物,抗撞击性，高
Braskem PE EF2126S3	LDPE	Braskem	低密度,光滑性,光学性能,抗结块性,可加工性，良好,通用
Braskem PE EF2222	LDPE	Braskem	低密度,低速凝固晶点,可加工性，良好
Braskem PE EP 340N	PP共聚物	Braskem	刚性，良好,共聚物,抗撞击性，良好,可加工性，良好,流动性中等
Braskem PE GP 100 BK	HDPE	Braskem	高 ESCR（抗应力开裂）,高分子量,高密度,抗紫外线性能良好,食品接触的合规性