LDPE Braskem PE EF2222 低密度,低速凝固晶点,可加工性，良好
材料简述：
EF2222 is a low-density polyethylene (LDPE), with excellent processability and low gel content. Those features allow production of thin and highly uniform films.
Additives:
No additives
Application:
Smooth or embossed films for diapers, disposable sheets, etc. Films for lamination. Injection-Blow Molding. Foamed applications.
Process:
Recommended processing conditions for film extrusion about 145 - 190 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.
材料物性
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.922 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD : 38 µm | 170 | MPa | ASTM D882 |
| 1% 正割, TD : 38 µm | 210 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 38 µm | 30.0 | MPa | ASTM D882 |
| TD : 断裂, 38 µm | 20.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 38 µm | 420 | % | ASTM D882 |
| TD : 断裂, 38 µm | 1100 | % | ASTM D882 |
| 落锤冲击 1(38 µm) | 70 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 38 µm | 480 | g | ASTM D1922 |
| TD : 38 µm | 150 | g | ASTM D1922 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (60°, 38.0 µm) | 100 | ASTM D2457 | |
| 雾度 | 6.0 | % | ASTM D1003 |
| 挤压说明 |
|---|
| Recommended Blow Film Extrusion Conditions: Temperature Profile: 145°C to 190°C Mass Temperature: 190°C Blow up Ratio: 2.0 to 3.0 : 1 Die Gap: 1.0 mm |
| 备注 | |
|---|---|
| 1 . | F50 |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE EP 340N | PP共聚物 | Braskem | 刚性，良好,共聚物,抗撞击性，良好,可加工性，良好,流动性中等 |
| Braskem PE GP 100 BK | HDPE | Braskem | 高 ESCR（抗应力开裂）,高分子量,高密度,抗紫外线性能良好,食品接触的合规性 |
| Braskem PE FP 33 | LLDPE | Braskem | 丁烯共聚单体,共聚物,光滑性,抗结块性,可加工性，良好 |
| Braskem PE GD5150K | HDPE | Braskem | 良好的电气性能,中等分子量 |
| Braskem PE GM5010T2U | HDPE | Braskem | 高 ESCR（抗应力开裂）,高分子量,高密度 |