LDPE Braskem PE EF2126S3 低密度,光滑性,光学性能,抗结块性,可加工性，良
材料简述：
EF2126S3 is a Low Density Polyethylene produced under high pressure conditions in an autoclave reactor. It offers excellent processability and optical properties.
Additives:
This resin contains slip and antiblock additives
Application:
This resin is recommended for use in extrusion of films for general purposes, technical films for automatic packaging and blends with LLDPE.
Process:
Blow Film Extrusion.
材料物性
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.921 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 2.6 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD : 38 µm | 160 | MPa | ASTM D882 |
| 1% 正割, TD : 38 µm | 200 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 38 µm | 25.0 | MPa | ASTM D882 |
| TD : 断裂, 38 µm | 20.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 38 µm | 290 | % | ASTM D882 |
| TD : 断裂, 38 µm | 1000 | % | ASTM D882 |
| 落锤冲击 1(38 µm) | 90 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 38 µm | 420 | g | ASTM D1922 |
| TD : 38 µm | 110 | g | ASTM D1922 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (60°, 38.0 µm) | 100 | ASTM D2457 | |
| 雾度 | 7.0 | % | ASTM D1003 |
| 挤压说明 |
|---|
| Recommended Blow Film Extrusion Conditions:Temperature Profile: 150°C to 165°CMass Temperature: 160°C to 165°CBlow up Ratio: 2.0 to 4.0 : 1Die Gap: 1.0 mmMinimum thickness:30 microns |
| 备注 | |
|---|---|
| 1 . | F50 |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE EF2222 | LDPE | Braskem | 低密度,低速凝固晶点,可加工性，良好 |
| Braskem PE EP 340N | PP共聚物 | Braskem | 刚性，良好,共聚物,抗撞击性，良好,可加工性，良好,流动性中等 |
| Braskem PE GP 100 BK | HDPE | Braskem | 高 ESCR（抗应力开裂）,高分子量,高密度,抗紫外线性能良好,食品接触的合规性 |
| Braskem PE FP 33 | LLDPE | Braskem | 丁烯共聚单体,共聚物,光滑性,抗结块性,可加工性，良好 |
| Braskem PE GD5150K | HDPE | Braskem | 良好的电气性能,中等分子量 |