材料简述：

---

Description:
H 125 is a high melt flow rate homopolymer designed for nonwoven by spunbonded processing. This resin features an excellent processing, allowing increased line speed or air pressure, besides gains on mechanical properties. The narrow molecular weight distribution, special stability and tight gel appearance control, provide its unique performance.

Applications:
High-performance spunbond nonwovens for hygiene disposables and hospital products; Nonwovens for furniture and decoration; Low-title and/or high-speed spinning multifilaments.

材料物性

基本信息
特性	均聚物 可加工性，良好 流动性高 窄分子量分布
用途	纺粘无纺布
机构评级	FDA 21 CFR 177.1520
形式	粒子
加工方法	纤维（纺纱）挤出

物理性能	额定值	单位制	测试方法
比重	0.905	g/cm³	ASTM D792, ISO 1183
熔流率（熔体流动速率） (230°C/2.16 kg)	38	g/10 min	ASTM D1238, ISO 1133

硬度	额定值	单位制	测试方法
洛氏硬度
R 级, 注塑	103		ASTM D785
R 计秤	103		ISO 2039-2

机械性能	额定值	单位制	测试方法
抗张强度 (屈服, 注塑)	33.0	MPa	ASTM D638, ISO 527-2
伸长率 (屈服, 注塑)	13	%	ASTM D638, ISO 527-2
弯曲模量 - 1% 正割
注塑	1300	MPa	ASTM D790
注塑	1400	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度
23°C, 注塑	25	J/m	ASTM D256
23°C, 注塑	2.7	kJ/m²	ISO 180

热性能	额定值	单位制	测试方法
载荷下热变形温度
0.45 MPa, 未退火, 注塑	95.0	°C	ASTM D648
0.45 MPa, 未退火	95.0	°C	ISO 75-2/B
1.8 MPa, 未退火, 注塑	55.0	°C	ASTM D648
1.8 MPa, 未退火	55.0	°C	ISO 75-2/A
维卡软化温度	154	°C	ISO 306/A, ASTM D1525 1

备注
1 .	压 力1 (10N)

相关牌号	种类	厂家	特性
Braskem PE HF0131	LLDPE	Braskem	低密度,抗氧化性,可加工性，良好,润滑
Braskem PE HF2007	LLDPE	Braskem	低密度,共聚物,抗穿孔性,抗氧化性,抗撞击性，高
Braskem PE HF3712	LLDPE	Braskem	低密度,高 ESCR（抗应力开裂）,抗氧化性,可加工性，良好,良好的熔体强度,润滑
Braskem PE HE 150	HDPE	Braskem	低速凝固晶点,丁烯共聚单体,钙含量，低（到无）,高密度,共聚物,抗氧化性,可加工性，良好,食品接触的合规性
Braskem PE HF2207B5	LLDPE	Braskem	低密度,共聚物,抗穿孔性,抗结块性,抗氧化性,抗撞击性，高