LHB118/21 AF is a LLDPE copolymer produced by Braskem. It is a ready-to-use product since it contains 10% LDPE. Its additive package was optimized to avoid blocking, even at low thickness. Film obtained from this grade show very good mechanical properties and a good balance between sealability and processability. Very low gel amount.
Additive:
Processing Aid Medium
Antioxidants Medium
Slip Medium
Antiblocking High
Applications: Frozen bags; general purpose.
材料物性
基本信息
添加剂
高抗结块性
加工助剂
抗氧化性
中度光滑性
特性
低密度
低速凝固晶点
高抗结块性
共聚物
抗氧化性
可加工性，良好
食品接触的合规性
中度光滑性
用途
包装
薄膜
通用
机构评级
FDA 21 CFR 177.1520
形式
粒子
加工方法
薄膜挤出
吹塑薄膜
挤出吹塑成型
物理性能
额定值
单位制
测试方法
比重
0.918
g/cm³
ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)
1.0
g/10 min
ASTM D1238
薄膜
额定值
单位制
测试方法
薄膜厚度 - 经测试
38
µm
抗张强度
ASTM D882
MD
: 断裂
40.0
MPa
ASTM D882
TD
: 断裂
30.0
MPa
ASTM D882
伸长率
ASTM D882
MD
: 断裂
1000
%
ASTM D882
TD
: 断裂
1300
%
ASTM D882
弯曲模量
ASTM D790
1% Secant, MD
180
MPa
ASTM D790
1% Secant, TD
210
MPa
ASTM D790
落锤冲击
100
g
ASTM D1709
埃尔曼多夫抗撕强度
ASTM D1922
MD
80
g
ASTM D1922
TD
560
g
ASTM D1922
光学性能
额定值
单位制
测试方法
光泽度 (60°)
98
ASTM D2457
雾度
12
%
ASTM D1003
挤压说明
Blown FilmTemperature profile: 170 to 190°CBlow up ratio: 2 to 3:1Die gap: 1.8 to 2.5 mmScreen package: 40/60/40 blendScreen package: 40/40 100% pureMass temperature: 190 °C