材料简述：

---

LF320 is a Linear Low Density Polyethylene, copolymer of butene-1, produced by gas fase process. Developed for cast film extrusion. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as processability. Very low gel amount. It contains processing aid and antioxidant additives.

Applications:
Stretch films; liners; LDPE and HDPE blends and packages for general use.

Process:
Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.

材料物性

基本信息
添加剂	加工助剂 抗氧化性
特性	低密度 低速凝固晶点 共聚物 光学性能 抗氧化性 可加工性，良好
用途	包装 薄膜 衬里 混合
机构评级	FDA 21 CFR 177.1520
形式	粒子
加工方法	流延薄膜

物理性能	额定值	单位制	测试方法
比重	0.919	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	2.7	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 断裂, 38 µm	30.0	MPa	ASTM D882
TD : 断裂, 38 µm	20.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 38 µm	1100	%	ASTM D882
TD : 断裂, 38 µm	1400	%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD : 38 µm	180	MPa	ASTM D790
1% Secant, TD : 38 µm	230	MPa	ASTM D790
落锤冲击 1(38 µm)	60	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 38 µm	60	g	ASTM D1922
TD : 38 µm	320	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (60°, 38.0 µm)	68		ASTM D2457
雾度	23	%	ASTM D1003

备注
1 .	F50

相关牌号	种类	厂家	特性
Braskem PE LD7000A	LDPE	Braskem	高 ESCR（抗应力开裂）,高强度,抗撞击性，高,可加工性，良好
Braskem PE LD7001A	LDPE	Braskem	低密度,高 ESCR（抗应力开裂）,光滑性,抗结块性,抗撞击性，高,可加工性，良好,收缩性低
Braskem PE LF-0720/20AF	LLDPE	Braskem	丁烯共聚单体,共聚物,光学性能,抗结块性,抗氧化性,可加工性，良好
Braskem PE PB-208	LDPE	Braskem	低密度,低粘度,可加工性，良好,良好的流动性,良好的柔韧性
Braskem PE LL-118/21	LLDPE	Braskem	低密度,低速凝固晶点,共聚物,光学性能,通用,中等抗结块性,中度光滑性