材料简述：

---

The resin ML3600S is a Linear Low Density Polyethylene, 1-hexene copolymer, developed for rotomolding. It presents an adequate balance of processability and mechanical properties, with good resistance to environmental stress cracking.

Applications:
Water tanks, tanks, parts for the automotive and agricultural segments.

Processing Conditions:
This resin is recommended to rotational molding under conditions comparable to polyethylene resins with similar melt index and density range. Oven Temperature Range: 260 to 350 °C. P.I.A.T:210 to 240°C.

Additives: Weathering resistance UV8 and antioxidants.

材料物性

基本信息
添加剂	抗氧化性 长期 UV-8 稳定剂
特性	低密度 高 ESCR（抗应力开裂） 抗紫外线性能良好 可加工性，良好
用途	农业应用 汽车领域的应用 水箱
机构评级	FDA 21 CFR 177.1520
形式	粒子
加工方法	滚塑成型 压缩模塑

物理性能	额定值	单位制	测试方法
密度	0.933	g/cm³	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	4.7	g/10 min	ASTM D1238
抗环境应力开裂 1			ASTM D1693
50°C, 2.00 mm, 10% Igepal, 模压成型, F50	250	hr	ASTM D1693
50°C, 2.00 mm, 100% Igepal, 模压成型, F50	> 1000	hr	ASTM D1693

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 模压成型	19.0	MPa	ASTM D638
断裂, 模压成型	29.0	MPa	ASTM D638
伸长率			ASTM D638
屈服, 模压成型	14	%	ASTM D638
断裂, 模压成型	> 1000	%	ASTM D638
弯曲模量 - 1% 正割 (模压成型)	770	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
Impact Strength			ARM
-40°C, 3.17 mm, 滚塑成形	55	J	ARM
-40°C, 6.34 mm, 滚塑成形	115	J	ARM

热性能	额定值	单位制	测试方法
载荷下热变形温度			ASTM D648
0.45 MPa, 未退火, 模压成型	60.0	°C	ASTM D648
1.8 MPa, 未退火, 模压成型	42.0	°C	ASTM D648
熔融峰值温度	127	°C	ASTM D3418

注射说明
Oven Temperature Range: 260 to 350 °C.

备注
1 .	0.3mm notched-plaques

相关牌号	种类	厂家	特性
Braskem PE ML3601U	LLDPE	Braskem	高 ESCR（抗应力开裂）,己烯共聚单体,抗氧化性,抗撞击性，高,抗紫外线性能良好
Braskem PE ML4400N	LLDPE	Braskem	刚性，高,高 ESCR（抗应力开裂）,抗氧化性,抗紫外线性能良好,可加工性，良好
Braskem PE LL-118	LLDPE	Braskem	低密度,低速凝固晶点,丁烯共聚单体,共聚物,光学性能,抗氧化性,可加工性，良好
Braskem PE LL6901S	LLDPE	Braskem	低速凝固晶点,丁烯共聚单体,共聚物,光学性能,可加工性，良好,良好的热封性,通用,中等抗结块性,中度光滑性
Braskem PE LL5801N	LLDPE	Braskem	光滑性,抗氧化性,辛烯共聚单体