材料简述：

---

Description:
LL118 is a Linear Low Density Polyethylene, copolymer of butene-1, produced by Spherilene process. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives.

Applications:
Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes.

材料物性

基本信息
添加剂	抗氧化性
特性	低密度 低速凝固晶点 丁烯共聚单体 共聚物 光学性能 抗氧化性 可加工性，良好
用途	包装 薄膜 衬里 混合
机构评级	FDA 21 CFR 177.1520
形式	粒子
加工方法	薄膜挤出 吹塑薄膜

物理性能	额定值	单位制	测试方法
密度	0.916	g/cm³	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	38	µm
抗张强度			ASTM D882
MD : 断裂	50.0	MPa	ASTM D882
TD : 断裂	40.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂	1100	%	ASTM D882
TD : 断裂	1400	%	ASTM D882
弯曲模量			ASTM D790
1% Secant, MD	180	MPa	ASTM D790
1% Secant, TD	200	MPa	ASTM D790
落锤冲击	120	g	ASTM D1709
埃尔曼多夫抗撕强度 - TD	370	g	ASTM D1922

光学性能	额定值		测试方法
光泽度 (60°)	48		ASTM D2457

挤出	额定值	单位制
熔体温度	170 到 210	°C

挤压说明
Blown FilmBlow up ratio: 2.2:1

相关牌号	种类	厂家	特性
Braskem PE LL6901S	LLDPE	Braskem	低速凝固晶点,丁烯共聚单体,共聚物,光学性能,可加工性，良好,良好的热封性,通用,中等抗结块性,中度光滑性
Braskem PE LL5801N	LLDPE	Braskem	光滑性,抗氧化性,辛烯共聚单体
Braskem PE LL218	LLDPE	Braskem	低密度,低速凝固晶点,丁烯共聚单体,共聚物,光学性能,可加工性，良好
Braskem PE LL6800N	LLDPE	Braskem	抗结块性,抗氧化性,辛烯共聚单体
Braskem PE LL-318	LLDPE	Braskem	低速凝固晶点,光学性能,可加工性，良好