LDPE Braskem PE PB-208 低密度,低粘度,可加工性，良好,良好的流动性,良好的
材料简述：
Description:
PB208 is a low density polyethylene with no additives. This grade shows excellent processability being indicated for low viscosity required applications. Injection molded products with this resin shows good flow and flexibility properties.
Additive:
No additives present
Applications:
Masterbatches;
Covers and injected parts with large flat area.
Process:
Injection Molding
材料物性
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.923 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 (50°C, 2.00 mm, 100% Igepal, 模压成型, F50) | 6.00 | hr | ASTM D1693 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 42 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服, 模压成型 | 10.0 | MPa | ASTM D638 |
| 断裂, 模压成型 | 6.00 | MPa | ASTM D638 |
| 伸长率 (断裂, 模压成型) | 140 | % | ASTM D638 |
| 弯曲模量 - 1% 正割 (模压成型) | 700 | MPa | ASTM D790 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 87.0 | °C | ASTM D1525 1 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 加工（熔体）温度 | 160 到 230 | °C | |
| 模具温度 | 5.00 到 25.0 | °C |
| 备注 | |
|---|---|
| 1 . | 压 力1 (10N) |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE LL-118/21 | LLDPE | Braskem | 低密度,低速凝固晶点,共聚物,光学性能,通用,中等抗结块性,中度光滑性 |
| Braskem PE LL-218/21 | LLDPE | Braskem | 低密度,共聚物,光学性能,可加工性，良好,中等抗结块性,中度光滑性 |
| Braskem PE ML3400N | LLDPE | Braskem | 低密度,高 ESCR（抗应力开裂）,抗氧化性,抗撞击性，高,抗紫外线性能良好,可加工性，良好,通用 |
| Braskem PE ML2400N | LLDPE | Braskem | 低翘曲性,丁烯共聚单体,良好的柔韧性,窄分子量分布 |
| Braskem PE ML3600S | LLDPE | Braskem | 低密度,高 ESCR（抗应力开裂）,抗紫外线性能良好,可加工性，良好 |