材料简述：

---

LD4003 is a Low Density Polyethylene produced under high pressure conditions in a tubular reactor. It offers good processability and excellent mechanical and optical properties.

Additives:
Slip and Antiblock

Application:
Films for general purposes, technical films for automatic packaging and blends with LLDPE.

Process:
Recommended processing conditions for film extrusion about 150 -165 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.

材料物性

基本信息
添加剂	抗结块剂 增滑剂
特性	光滑性 光学性能 抗结块性 可加工性，良好
用途	薄膜 混合
加工方法	薄膜挤出

物理性能	额定值	单位制	测试方法
比重	0.922	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	1.9	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
割线模量			ASTM D882
1% 正割, MD : 70 µm, 吹塑薄膜	145	MPa	ASTM D882
1% 正割, TD : 70 µm, 吹塑薄膜	150	MPa	ASTM D882
抗张强度			ASTM D882
MD : 断裂, 70 µm, 吹塑薄膜	25.0	MPa	ASTM D882
TD : 断裂, 70 µm, 吹塑薄膜	20.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 70 µm, 吹塑薄膜	590	%	ASTM D882
TD : 断裂, 70 µm, 吹塑薄膜	920	%	ASTM D882
落锤冲击 (70 µm, 吹塑薄膜)	140	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 70 µm, 吹塑薄膜	460	g	ASTM D1922
TD : 70 µm, 吹塑薄膜	300	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度			ASTM D2457
45°, 70.0 µm, 吹塑薄膜	79		ASTM D2457
60°, 70.0 µm, 吹塑薄膜	116		ASTM D2457
雾度 (70.0 µm, 吹塑薄膜)	7.0	%	ASTM D1003

相关牌号	种类	厂家	特性
Braskem PE LD5010FC	LDPE	Braskem	低速凝固晶点,通用,无添加剂
PROXESS 1806S3	LLDPE	Braskem	共聚物,光滑性,抗结块性,抗氧化性,可加工性，良好,良好的撕裂强度
PLURIS 4303	LLDPE	Braskem	低速凝固晶点,刚性，高,可加工性，良好,韧性良好,中等抗结块性,中度光滑性
Braskem PE LL4405S	LLDPE	Braskem	低速凝固晶点,高光滑性,高抗结块性,可加工性，良好
Braskem PE LL4801N	LLDPE	Braskem	光学性能,抗氧化性,可加工性，良好