LDPE Braskem PE PB-608 低密度,良好的流动性,良好的柔韧性,耐高压加热性
材料简述：
Description:
PB608 is a grade produced under high pressure in an autoclave reactor. This grade is especially designed for injection molding of articles that must show excellent flexibility properties and very good flow ability.
Additive:
No additives present.
Applications:
Masterbatches;
Covers and injected parts with large flat area.
Process:
Injection Molding
材料物性
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.915 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 (50°C, 2.00 mm, 10% Igepal, 模压成型, F50) | 15.0 | hr | ASTM D1693 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 39 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服, 模压成型 | 8.00 | MPa | ASTM D638 |
| 断裂, 模压成型 | 8.00 | MPa | ASTM D638 |
| 伸长率 (断裂, 模压成型) | 390 | % | ASTM D638 |
| 弯曲模量 - 1% 正割 (模压成型) | 450 | MPa | ASTM D790 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 79.0 | °C | ASTM D1525 1 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 加工（熔体）温度 | 180 到 210 | °C | |
| 模具温度 | 5.00 到 25.0 | °C |
| 备注 | |
|---|---|
| 1 . | 压 力1 (10N) |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE MR-435UV | LLDPE | Braskem | 低密度,丁烯共聚单体,刚性，良好,高 ESCR（抗应力开裂）,可加工性，良好 |
| Braskem PE JV060U | HDPE | Braskem | 尺寸稳定性良好,丁烯共聚单体,刚性，高,高密度,共聚物,抗氧化性,抗紫外线性能良好,可加工性，良好,良好的强度,耐低温冲击,食品接触的合规性,窄分子量分布 |
| Braskem PE LH-218 | LLDPE | Braskem | 低密度,低速凝固晶点,共聚物,光学性能 |
| Braskem PE LH-118 | LLDPE | Braskem | 低密度,低速凝固晶点,共聚物,光学性能,己烯共聚单体,抗氧化性,可加工性，良好,食品接触的合规性 |
| Braskem PE LH-537 | LLDPE | Braskem | 低速凝固晶点,刚性，良好,可加工性，良好,柔软,食品接触的合规性 |