材料简述：

---

HT5303 is a high density polyethylene, hexene copolymer, produced through Unipol® process and developed for the manufacturing of corrugated pipes. It exhibits an appropriate balance between stiffness, impact and stress cracking resistance, as well as a high resistance to oxidative degradation.

Application:
Corrugated pipes for energy and telecom cables protection and for drainage of roads and sports fields.

Process:
Pipe Extrusion.

材料物性

基本信息
特性	刚性，良好 高 ESCR（抗应力开裂） 己烯共聚单体 抗撞击性，良好
用途	波纹管 管道系统
机构评级	FDA 21 CFR 177.1520
加工方法	管路挤出成型

物理性能	额定值	单位制	测试方法
比重	0.954	g/cm³	ASTM D792
熔流率（熔体流动速率）			ASTM D1238
190°C/2.16 kg	0.30	g/10 min	ASTM D1238
190°C/21.6 kg	26	g/10 min	ASTM D1238
抗环境应力开裂			ASTM D1693
50°C, 2.00 mm, 10% Igepal, 模压成型, F50	43.0	hr	ASTM D1693
50°C, 2.00 mm, 100% Igepal, 模压成型, F50	168	hr	ASTM D1693

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 模压成型)	64		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 模压成型	30.0	MPa	ASTM D638
断裂, 模压成型	33.0	MPa	ASTM D638
弯曲模量 - 1% 正割 (模压成型)	1140	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (模压成型)	100	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度 (0.45 MPa, 未退火, 模压成型)	128	°C	ASTM D648
维卡软化温度	66.0	°C	ASTM D1525 1
氧感应时间 2(200°C)	> 25	min	ASTM D3895

补充信息	额定值	单位制	测试方法
NCLS 3	> 24	hr	ASTM F2136

备注
1 .	压 力1 (10N)
2 .	Compression Molded
3 .	Compression Molded

相关牌号	种类	厂家	特性
Braskem PE HS5502XP	HDPE	Braskem	高 ESCR（抗应力开裂）,共聚物,可加工性，良好
Braskem PE SGF4950HS	HDPE	Braskem	高 ESCR（抗应力开裂）,共聚物,可更新资源,可加工性，良好
Braskem PE SHC7260LSL	HDPE	Braskem	UV Stabilized,低翘曲性,刚性，高,可更新资源,硬度高
Braskem PE GM5255	HDPE	Braskem	高 ESCR（抗应力开裂）,可加工性，良好,双峰型分子量分布
Braskem PE GM7040GCF	HDPE	Braskem	UV Stabilized,高 ESCR（抗应力开裂）,高分子量,双峰型分子量分布