LLDPE Flexus 9212XP 高光滑性,己烯共聚单体,抗穿孔性,抗撞击性，良好,良好的加
材料简述：
Braskem Flexus9212XP is a LLDPE hexene copolymer produced through metallocene catalyst which presents excellent impact and puncture strength, beyond a differential sealing performance comparing with another typical LLDPE. It contains a special package of slip additives which allow better CoF control after lamination.
Applications:
Films laminated for automatic packaging (FFS) of solids and liquids, co extrusion and general use.
Additive:
Slip package in high level
Blocking medium
Processing Aids Medium Level
材料物性
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.917 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 1 | 40 | µm | |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂 | 35.0 | MPa | ASTM D882 |
| TD : 断裂 | 25.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂 | 850 | % | ASTM D882 |
| TD : 断裂 | 840 | % | ASTM D882 |
| 弯曲模量 | ASTM D790 | ||
| 1% Secant, MD | 150 | MPa | ASTM D790 |
| 1% Secant, TD | 160 | MPa | ASTM D790 |
| 落锤冲击 | > 850 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD | 230 | g | ASTM D1922 |
| TD | 790 | g | ASTM D1922 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (60°) | 84 | ASTM D2457 | |
| 雾度 | 7.0 | % | ASTM D1003 |
| 备注 | |
|---|---|
| 1 . | Processed with 10% of LDPE in a 75mm screw diameter extruder with blow up ratio of 2.2:1 |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Flexus 7200 | LLDPE | Braskem | 共聚物,己烯共聚单体,抗穿孔性,抗氧化性,抗撞击性，良好,可加工性，良好 |
| Flexus 9200 | LLDPE | Braskem | 己烯共聚单体,抗穿孔性,抗氧化性,抗撞击性，良好,可加工性，良好 |
| Flexus 9211 | LLDPE | Braskem | 己烯共聚单体,抗穿孔性,抗撞击性，良好 |
| Ipiranga GF 4960 | HDPE | Braskem | 刚性，高,高密度,均聚物,抗撞击性，高,可加工性，良好,食品接触的合规性 |
| Braskem PP H 614 | PP均聚物 | Braskem | 均聚物,可加工性，良好,流动性低 |