材料简述：

---

INSPIRE™ 137 Performance Polymer, is a high melt strength resin which provides bubble stability, low gel content and can be used as blend partner to make more cost effective films on all types of conventional blown film lines.

INSPIRE 137 Performance Polymer can be suggested for film and sheet extrusion.

INSPIRE 137 Performance Polymer exhibits:

• High Melt Strength

• Excellent Processability

• Low gel content

• High Impact and Puncture Resistance

• Stiffness/Toughness Balance

• Temperature Resistance

Complies with:

• U.S. FDA 21 CFR 177.1520(c)3.2a

• European Commission Regulation (EU) No 10/2011

Consult the regulations for detailed information.

材料物性

基本信息
机构评级	FDA 21 CFR 177.1520(c) 3.2a 欧洲 No 10/2011
形式	粒子

物理性能	额定值	单位制	测试方法
密度	0.900	g/cm³	ISO 1183
熔流率（熔体流动速率） (230°C/2.16 kg)	0.80	g/10 min	ISO 1133

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	50	µm
膜刺穿强度 (50 µm)	4.40	J	ASTM D5748
膜刺穿力 (50 µm)	92.0	N	ASTM D5748
拉伸模量			ISO 527-3
2% 正割, MD : 50 µm	624	MPa	ISO 527-3
2% 正割, TD : 50 µm	584	MPa	ISO 527-3
拉伸应力			ISO 527-3
MD : 屈服, 50 µm	34.0	MPa	ISO 527-3
TD : 屈服, 50 µm	24.0	MPa	ISO 527-3
MD : 断裂, 50 µm	50.0	MPa	ISO 527-3
TD : 断裂, 50 µm	36.0	MPa	ISO 527-3
伸长率			ISO 527-3
MD : 断裂, 50 µm	590	%	ISO 527-3
TD : 断裂, 50 µm	670	%	ISO 527-3
落锤冲击 (50 µm)	160	g	ISO 7765-1/A
埃尔曼多夫抗撕强度			ASTM D1922
MD : 50 µm	26	g	ASTM D1922
TD : 50 µm	57	g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (45°, 50.0 µm)	19		ASTM D2457
雾度 (50.0 µm)	36	%	ISO 14782

挤出	额定值	单位制
熔体温度	230	°C

挤压说明
吹塑薄膜的制造条件： 模具间隙：1.0 mm 熔体温度：230°C 放大比：2.5:1

相关牌号	种类	厂家	特性
INSPIRE™ 147	PP，未指定	Braskem Europe GmbH
INSPIRE™ 150	抗撞击PP均聚物	Braskem Europe GmbH
INSPIRE™ 136	抗撞击PP均聚物	Braskem Europe GmbH
INSPIRE™ 114 EU	PP，未指定	Braskem Europe GmbH
Braskem PP DH742.01	PP均聚物	Braskem Europe GmbH	Excellent Organoleptic Properties,成核的,尺寸稳定性良好,光学性能,均聚物,抗静电性,可加工性，良好,快的成型周期,流动性中等,清晰度，高,收缩性低