LLDPE Braskem PE SLH0820/30AF 低速凝固晶点,抗结块性,可更新资源,食
材料简述：
Description:
SLH0820/30AF is a LLDPE hexene copolymer produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount.
The minimum biobased content of this grade is 84%, determined according to ASTM D6866.
Additive:
Slip Absent
Processing Aid Medium
Antiblocking High
Applications:
Lamination
Heavy duty bags
Blends with LDPE and HDPE
Valvulated heavy duty bags
材料物性
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.920 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 25 µm | 50.0 | MPa | ASTM D882 |
| TD : 断裂, 25 µm | 40.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 25 µm | 950 | % | ASTM D882 |
| TD : 断裂, 25 µm | 1200 | % | ASTM D882 |
| 弯曲模量 | ASTM D790 | ||
| 1% Secant, MD : 25 µm | 170 | MPa | ASTM D790 |
| 1% Secant, TD : 25 µm | 180 | MPa | ASTM D790 |
| 落锤冲击 1 | 170 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 25 µm | 270 | g | ASTM D1922 |
| TD : 25 µm | 500 | g | ASTM D1922 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 生物质含量 | > 84 | % | ASTM D6866 |
| 挤压说明 |
|---|
| Blown Films Temperature Profile: from 180 to 210°C Blow up Ratio: from 2 to 3:1 Die Gap: from 1.8 to 2.5 mm Screen Package(Mesh): 40/40 - 100% pure 40/60/40 - blend Mass temperature: 220°C (max 230°C) |
| 备注 | |
|---|---|
| 1 . | F50 |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE SHE150 | HDPE | Braskem | 低速凝固晶点,共聚物,抗氧化性,可更新资源,可加工性，良好,良好的加工稳定性,食品接触的合规性 |
| Braskem PE SLH118 | LLDPE | Braskem | 低速凝固晶点,抗氧化性,可更新资源,食品接触的合规性 |
| Braskem PE SLL218/21 | LLDPE | Braskem | 光学性能,可更新资源,食品接触的合规性 |
| Braskem PE SLH218 | LLDPE | Braskem | 低速凝固晶点,可更新资源,食品接触的合规性,通用 |
| Braskem PE SLL118 | LLDPE | Braskem | 低速凝固晶点,抗氧化性,可更新资源,食品接触的合规性 |