HDPE Braskem PE HDF1050 刚性，高,高分子量,良好的热封性,食品接触的合规性
材料简述：
HDF1050 is a high molecular weight high density polyethylene copolymer with broad bimodal weight distribution developed for the blown film segment. Films made with this degree offer high stiffness, good heat sealing response, and resistance to trait propagation. This material meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1520.
Applications:
Very thin film on high-speed line, low caliber.
Process:
Blown Film Extrusion
材料物性
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.950 | g/cm³ | ASTM D4883 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 190°C/2.16 kg | 0.060 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 9.5 | g/10 min | ASTM D1238 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 流量 : 屈服 | 30.0 | MPa | ASTM D638 |
| 横向流量 : 屈服 | 26.0 | MPa | ASTM D638 |
| 流量 : 断裂 | 75.0 | MPa | ASTM D638 |
| 横向流量 : 断裂 | 47.0 | MPa | ASTM D638 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD | 760 | MPa | ASTM D882 |
| 1% 正割, TD | 940 | MPa | ASTM D882 |
| 落锤冲击 | 360 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD | 40 | g | ASTM D1922 |
| TD | 90 | g | ASTM D1922 |
| 相关牌号 | 种类 | 厂家 | 特性 |
|---|---|---|---|
| Braskem PE HDI0661U1 | HDPE | Braskem IDESA | 刚性，良好,共聚物,抗撞击性，良好,窄分子量分布 |
| Braskem PE HDB0355 | HDPE | Braskem IDESA | 高 ESCR（抗应力开裂）,共聚物 |
| Braskem PE HDI0861U1 | HDPE | Braskem IDESA | Good Rigidity,共聚物,抗撞击性，良好,优良外观,窄分子量分布 |
| Braskem PE HDI2061 | HDPE | Braskem IDESA | 刚性，高,共聚物,可加工性，良好,良好的流动性,通用,硬度高,窄分子量分布 |
| Braskem PE HDP0353 | HDPE | Braskem IDESA | 共聚物,双峰型分子量分布 |